Hot Rolled Steel Sheets & Strips for Deep Drawing
Designación | Espesor (mm) |
Composición química (% en peso) | ||||||
---|---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | Sol-Al | etc | ||
POSHRD2 | 1.8~7.0 | ~0.03 | ~0.03 | ~0.25 | ~0.02 | ~0.02 | ~0.06 | - |
POSHRD2 | 2.0~7.0 | ~0.005 | ~0.03 | ~0.20 | ~0.02 | ~0.02 | ~0.06 | Ti 0.005~0.05 Nb 0.005~0.04 |
POSHRD3 | 2.0~7.0 | ~0.005 | ~0.03 | ~0.20 | ~0.02 | ~0.02 | ~0.06 | Ti 0.01~0.06 |
Acero resistente al ácido sulfúrico y placas y tiras resistentes a la intemperie
Designación | Espesor (mm) |
Composición química (wt.%) | |||||
---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | Others | ||
ANCOR-H | 1.8~7.0 | ~0.10 | ~0.50 | ~1.70 | ~0.035 | ~0.035 | Cu ~0.50 Cr ~0.50 |
HICON700W | 2.3~6.5 | ~0.12 | ~0.45 | ~2.50 | ~0.035 | ~0.01 | Cu ~0.55 Cr ~1.20 |
Designación | Punto de rendimiento (MPa) |
Resistencia a la tracción (MPa) |
Alargamiento | Prueba de flexión | |||
---|---|---|---|---|---|---|---|
Pieza de prueba | % | Ángulo de flexión | Diámetro interior | Pieza de prueba/Dirección | |||
ANCOR-H | 245~ | 400~ | No.5 Rolling Direction | 25 | 180° | 1.5t | JIS No.1/ Traverse |
HICON700W | 700~ | 750~950 | No.5 Rolling Direction | 12 | 90° | 1.0t | JIS No.5/ Traverse |
Hojas y tiras de acero laminado en caliente para estructuras de automóviles
Designación | Espesor (mm) |
Composición química (wt.%) | |||||
---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | Nb | ||
ATOS540(ATOS55) | 2.3~12.7 | ~0.20 | ~0.40 | ~1.50 | ~0.03 | ~0.03 | Added |
ATOS590(ATOS60) | 2.3~12.7 | ~0.20 | ~0.40 | ~1.50 | ~0.03 | ~0.03 | |
ATOS780(ATOS80) | 2.3~14 | ~0.20 | ~0.40 | ~2.00 | ~0.03 | ~0.03 | |
ATOS980(ATOS100) | 4~8.0 | ~0.20 | ~0.40 | ~2.00 | ~0.03 | ~0.03 |
Designación | Prueba de tracción | Prueba de flexión | ||||||
---|---|---|---|---|---|---|---|---|
Resistencia a la tracción (MPa) |
Punto de rendimiento (MPa) |
Alargamiento(%), Grosor(mm) *Laminado | Resistencia a la flexión | Diámetro interior | Pieza de prueba (JIS No.3) |
|||
No.5 Test Piece 2.5-5.0 |
No.5 Test Piece 5.0-6.3 |
No.1A Test Piece 6.3-12.7 |
||||||
ATOS540(ATOS55) | 540~ | 340~ | 20~ | 21~ | 14~ | 180° | 1.5t | Traverse |
ATOS590(ATOS60) | 590~ | 420~ | 19~ | 20~ | 13~ | 180° | 1.5t | Traverse |
ATOS780(ATOS80) | 780~ | 700~ | 14~ | 14~ | 9~ | 180° | 1.5t | Traverse |
ATOS980(ATOS100) | 980 | 880 | 8~ (No.5 test piece applied) | 90° | 3.0t | Traverse |
Placas y tiras laminadas en caliente para vigas de impacto y estabilizadores de automóviles
Designación | Espesor (mm) |
Composición química (% en peso) | |||||||
---|---|---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | Sol-Al | Cr | B | ||
AUTOBEAM | 1.6~7.0 | ~0.30 | - | ~1.50 | - | ~0.005 | ~0.12 | 0.10~0.30 | - |
STAB | 1.6~7.0 | ~0.30 | ~0.25 | ~1.00 | ~0.025 | ~0.015 | ~0.10 | 0.20~0.40 | 0.001~0.005 |
Designación | Resistencia a la tracción (MPa) | Test de doblado | Nota | |
---|---|---|---|---|
Ángulo de flexión | Diámetro interno | |||
AUTOBEAM | 490~784 | 180° | 1.5t | Los productos terminados requieren el tratamiento térmico adecuado para estar completos |
The tables below represent the thickness and width of products available. These dimensions are subject to change.
Please contact our sales representative before placing an order
Product | Available Dimension (mm) | Available Dimension for Each Thickness (mm) | |
---|---|---|---|
Thickness | Width | ||
Hot Rolled Steel Plate TS 300MPa Class | Thickness: 0.8-24.0 Width: 650-1950 |
0.8~1.1 | 650~1000 |
1.2~2.0 | 650~1570 | ||
2.0~3.0 | 650~1800 | ||
3.0~24.0 | 650~1950 | ||
Hot Rolled Steel Plate TS 400MPa Class | Thickness: 1.1-24.0 Width: 700-1950 |
1.1~1.8 | 700~1500 |
1.9~3.0 | 700~1720 | ||
3.0~4.5 | 700~1800 | ||
4.5~24.0 | 700~1950 | ||
Hot Rolled Steel Plate TS 500MPa Class | Thickness: 1.4-22.0 Width: 700-1950 |
1.4~1.6 | 700~1420 |
1.7~2.3 | 700~1570 | ||
2.3~3.0 | 700~1720 | ||
3.0~22.0 | 700~1950 | ||
Hot Rolled Steel Plate TS 600MPa Class | Thickness: 1.4-22.0 Width: 700-1950 |
1.4~2.0 | 700~1420 |
2.0~3.0 | 700~1650 | ||
3.0~22.0 | 700~1950 | ||
Hot Rolled Steel Plate TS 800MPa Class | Thickness: 3.2-14.0 Width: 1120-1620 |
3.2~6.0 | 1120~1495 |
6.0~12.0 | 1120~1620 | ||
12.0~14.0 | 1120~1420 | ||
Checkered Plate TS 300MPa Class | Thickness: 3.0-7.0 Width: 900-1250 |
3.0~7.0 | 900~1250 |
P/O Plate | Thickness: 1.2-8.0 Width: 900-1250 |
1.2~1.8 | 650~1400 |
1.8~6.0 | 650~1650 | ||
6.0~8.0 | 650~1400 |
El Galvanizado en caliente es un proceso que consiste en la aplicación de recubrimiento superficial de zinc sobre elemento de hierro y acero mediante la inmersión de zinc fundido a una temperatura de 450°C.. El objetivo de este proceso es conseguir la protección de las piezas o elementos metálicos frente a la corrosión por humedad y/o contaminación ambiental.
El Galvanneal es un proceso donde el acero se sumerge en un baño caliente de zinc (similar al proceso de Galvanizado), luego es sometido a un proceso secundario en el que el hierro se recuece con el revestimiento de zinc para crear una mezcla de hierro - zinc en la superficie del metal. El Galvanneal proporciona mayores beneficios en procesos tales como soldabilidad, pintura, formalidad y resistencia a la corrosión
Los productos de acero inoxidable se pueden clasificar en acero inoxidable austenítico, acero inoxidable ferrítico y acero inoxidable martensítico según sus componentes de aleación y estructura de tejido. Sus aplicaciones típicas incluyen tubos de escape de automóviles, electrodomésticos de cocina, electrónica y materiales de construcción. Las aplicaciones emergentes incluyen sectores ecológicos, como cajas de baterías EV y GNL.
¿Tienes alguna duda, comentario o estás interesado en alguno de nuestros productos? ¡No dudes en enviarnos un mensaje!
Líderes en la industria de la acerería integrada
POSCO MPPC © 2023 Todos los derechos reservados
AVISO DE PRIVACIDAD