Hot Rolled Steel Sheets & Strips for Deep Drawing
Designation | Thickness (mm) |
Chemical Composition(wt.%) | ||||||
---|---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | Sol-Al | 기타 | ||
POSHRD2 | 1.8~7.0 | ~0.03 | ~0.03 | ~0.25 | ~0.02 | ~0.02 | ~0.06 | - |
POSHRD2 | 2.0~7.0 | ~0.005 | ~0.03 | ~0.20 | ~0.02 | ~0.02 | ~0.06 | Ti 0.005~0.05 Nb 0.005~0.04 |
POSHRD3 | 2.0~7.0 | ~0.005 | ~0.03 | ~0.20 | ~0.02 | ~0.02 | ~0.06 | Ti 0.01~0.06 |
Sulfuric Acid Resistant Steel and Plates & Strips Resistant to Weathering
Designation | Thickness (mm) |
Chemical Composition(wt.%) | |||||
---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | Others | ||
ANCOR-H | 1.8~7.0 | ~0.10 | ~0.50 | ~1.70 | ~0.035 | ~0.035 | Cu ~0.50 Cr ~0.50 |
HICON700W | 2.3~6.5 | ~0.12 | ~0.45 | ~2.50 | ~0.035 | ~0.01 | Cu ~0.55 Cr ~1.20 |
Designation | Yield Point (MPa) |
Tensile Strength (MPa) |
Elongation | Bending Test | |||
---|---|---|---|---|---|---|---|
Test Piece | % | Bending Angle | Inner Diameter | Test Piece/Direction | |||
ANCOR-H | 245~ | 400~ | No.5 Rolling Direction | 25 | 180° | 1.5t | JIS No.1/ Traverse |
HICON700W | 700~ | 750~950 | No.5 Rolling Direction | 12 | 90° | 1.0t | JIS No.5/ Traverse |
Hot Rolled Steel Sheets & Strips for Car Structures
Designation | Thickness (mm) |
Chemical Composition(wt.%) | |||||
---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | Nb | ||
ATOS540(ATOS55) | 2.3~12.7 | ~0.20 | ~0.40 | ~1.50 | ~0.03 | ~0.03 | Added |
ATOS590(ATOS60) | 2.3~12.7 | ~0.20 | ~0.40 | ~1.50 | ~0.03 | ~0.03 | |
ATOS780(ATOS80) | 2.3~14 | ~0.20 | ~0.40 | ~2.00 | ~0.03 | ~0.03 | |
ATOS980(ATOS100) | 4~8.0 | ~0.20 | ~0.40 | ~2.00 | ~0.03 | ~0.03 |
Designation | Tensile Test | Bending Test | ||||||
---|---|---|---|---|---|---|---|---|
Tensile Strength (MPa) |
Yield Point (MPa) |
Elongation(%), Thickness(mm) *Rolling | Bending Strength | Inner Diameter | Test Piece (JIS No.3) |
|||
No.5 Test Piece 2.5-5.0 |
No.5 Test Piece 5.0-6.3 |
No.1A Test Piece 6.3-12.7 |
||||||
ATOS540(ATOS55) | 540~ | 340~ | 20~ | 21~ | 14~ | 180° | 1.5t | Traverse |
ATOS590(ATOS60) | 590~ | 420~ | 19~ | 20~ | 13~ | 180° | 1.5t | Traverse |
ATOS780(ATOS80) | 780~ | 700~ | 14~ | 14~ | 9~ | 180° | 1.5t | Traverse |
ATOS980(ATOS100) | 980 | 880 | 8~ (No.5 test piece applied) | 90° | 3.0t | Traverse |
Hot Rolled Plates and Strips for Car Impact Beams and Stabilizers
Designation | Thickness (mm) |
Chemical Composition(wt.%) | |||||||
---|---|---|---|---|---|---|---|---|---|
C | Si | Mn | P | S | Sol-Al | Cr | B | ||
AUTOBEAM | 1.6~7.0 | ~0.30 | - | ~1.50 | - | ~0.005 | ~0.12 | 0.10~0.30 | - |
STAB | 1.6~7.0 | ~0.30 | ~0.25 | ~1.00 | ~0.025 | ~0.015 | ~0.10 | 0.20~0.40 | 0.001~0.005 |
Designation | Tensile Strength(MPa) | Bending Test | Note | |
---|---|---|---|---|
Bending Angle | Inner Diameter | |||
AUTOBEAM | 490~784 | 180° | 1.5t | Finished goods require the appropriate heat treatment to be complete |
The tables below represent the thickness and width of products available. These dimensions are subject to change.
Please contact our sales representative before placing an order
Product | Available Dimension (mm) | Available Dimension for Each Thickness (mm) | |
---|---|---|---|
Thickness | Width | ||
Hot Rolled Steel Plate TS 300MPa Class | Thickness: 0.8-24.0 Width: 650-1950 |
0.8~1.1 | 650~1000 |
1.2~2.0 | 650~1570 | ||
2.0~3.0 | 650~1800 | ||
3.0~24.0 | 650~1950 | ||
Hot Rolled Steel Plate TS 400MPa Class | Thickness: 1.1-24.0 Width: 700-1950 |
1.1~1.8 | 700~1500 |
1.9~3.0 | 700~1720 | ||
3.0~4.5 | 700~1800 | ||
4.5~24.0 | 700~1950 | ||
Hot Rolled Steel Plate TS 500MPa Class | Thickness: 1.4-22.0 Width: 700-1950 |
1.4~1.6 | 700~1420 |
1.7~2.3 | 700~1570 | ||
2.3~3.0 | 700~1720 | ||
3.0~22.0 | 700~1950 | ||
Hot Rolled Steel Plate TS 600MPa Class | Thickness: 1.4-22.0 Width: 700-1950 |
1.4~2.0 | 700~1420 |
2.0~3.0 | 700~1650 | ||
3.0~22.0 | 700~1950 | ||
Hot Rolled Steel Plate TS 800MPa Class | Thickness: 3.2-14.0 Width: 1120-1620 |
3.2~6.0 | 1120~1495 |
6.0~12.0 | 1120~1620 | ||
12.0~14.0 | 1120~1420 | ||
Checkered Plate TS 300MPa Class | Thickness: 3.0-7.0 Width: 900-1250 |
3.0~7.0 | 900~1250 |
P/O Plate | Thickness: 1.2-8.0 Width: 900-1250 |
1.2~1.8 | 650~1400 |
1.8~6.0 | 650~1650 | ||
6.0~8.0 | 650~1400 |
El Galvanizado en caliente es un proceso que consiste en la aplicación de recubrimiento superficial de zinc sobre elemento de hierro y acero mediante la inmersión de zinc fundido a una temperatura de 450°C.. El objetivo de este proceso es conseguir la protección de las piezas o elementos metálicos frente a la corrosión por humedad y/o contaminación ambiental.
El Galvanneal es un proceso donde el acero se sumerge en un baño caliente de zinc (similar al proceso de Galvanizado), luego es sometido a un proceso secundario en el que el hierro se recuece con el revestimiento de zinc para crear una mezcla de hierro - zinc en la superficie del metal. El Galvanneal proporciona mayores beneficios en procesos tales como soldabilidad, pintura, formalidad y resistencia a la corrosión
Los productos de acero inoxidable se pueden clasificar en acero inoxidable austenítico, acero inoxidable ferrítico y acero inoxidable martensítico según sus componentes de aleación y estructura de tejido. Sus aplicaciones típicas incluyen tubos de escape de automóviles, electrodomésticos de cocina, electrónica y materiales de construcción. Las aplicaciones emergentes incluyen sectores ecológicos, como cajas de baterías EV y GNL.
Do you have any questions? comments or are you interested in any of our products? Don't hesitate to send us a message!